CN103286320A - 用于太阳能电池的超细银粉的制备方法 - Google Patents

用于太阳能电池的超细银粉的制备方法 Download PDF

Info

Publication number
CN103286320A
CN103286320A CN2013102269380A CN201310226938A CN103286320A CN 103286320 A CN103286320 A CN 103286320A CN 2013102269380 A CN2013102269380 A CN 2013102269380A CN 201310226938 A CN201310226938 A CN 201310226938A CN 103286320 A CN103286320 A CN 103286320A
Authority
CN
China
Prior art keywords
silver powder
solar cell
super fine
fine silver
reducing solution
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2013102269380A
Other languages
English (en)
Inventor
龚伟华
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Zheng Yulin
Original Assignee
SUZHOU NUOXIN INNOVATION ENERGY CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SUZHOU NUOXIN INNOVATION ENERGY CO Ltd filed Critical SUZHOU NUOXIN INNOVATION ENERGY CO Ltd
Priority to CN2013102269380A priority Critical patent/CN103286320A/zh
Publication of CN103286320A publication Critical patent/CN103286320A/zh
Pending legal-status Critical Current

Abstract

本发明提供了一种用于太阳能电池的超细银粉的制备方法，包括以下步骤：（1）将抗坏血酸溶液加热至50-60摄氏度，加入分散剂的同时进行搅拌，加入后继续搅拌3-3.5小时，得到还原性溶液，在还原性溶液中加入无水酒精和甲醛，搅拌30分钟，冷却至室温；（2）将还原性溶液和硝酸银溶液分别加热至反应温度，将硝酸银溶液加入到还原性溶液中，搅拌；（3）将反应后的反应物沉淀，过滤，洗涤，然后恒温干燥；（4）将干燥后的固体过20微米筛，得到超细银粉；（5）将超细银粉用于太阳能电池的正面银浆。相较于现有技术，本发明的制备方法所获得的超细银粉的纯度较高，可以提高太阳能电池的转换效率。

Description

用于太阳能电池的超细银粉的制备方法
技术领域
本发明涉及一种制备方法，尤其涉及一种用于太阳能电池的超细银粉的制备方法。
背景技术
电池已经广泛应用在众多场合和产品上，其中电池的效率一直是人们想要提高的目标。人们从各方面进行了努力，以希望提高电池的效率，例如从新材料、新制备方法等。太阳能电池的表面通常会涂覆银浆，其对太阳能电池的能量转换效率有着很大的影响因素，因此从如何改善银浆的性能成为一个研究的方向。
发明内容
本发明主要解决的技术问题是如何提高超细银粉的纯度，对应提高太阳能电池的转换效率。
为了解决上述技术问题，本发明实施例公开了一种用于太阳能电池的超细银粉的制备方法，包括以下步骤：
（1）、将抗坏血酸溶液加热至50-60摄氏度，加入分散剂的同时进行搅拌，加入后继续搅拌3-3.5小时，得到还原性溶液，在还原性溶液中加入无水酒精和甲醛，搅拌30分钟，冷却至室温；
（2）、将还原性溶液和硝酸银溶液分别加热至反应温度，将硝酸银溶液加入到还原性溶液中，搅拌；
（3）、将反应后的反应物沉淀，过滤，洗涤，然后恒温干燥；
（4）、将干燥后的固体过20微米筛，得到超细银粉；
（5）、将超细银粉用于太阳能电池的正面银浆。
在本发明的一较佳实施例中，步骤（1）中的抗坏血酸溶液加热温度为55摄氏度，继续搅拌时间为200分钟。
在本发明的一较佳实施例中，步骤（2）中反应温度为120摄氏度。
在本发明的一较佳实施例中，步骤（3）中洗涤用去离子水或者无水酒精。
在本发明的一较佳实施例中，步骤（4）中的恒温为75摄氏度，干燥时间为3.2小时。
在本发明的一较佳实施例中，步骤（1）中分散剂为羧甲基纤维素。
相较于现有技术，本发明的制备方法所获得的超细银粉的纯度较高，可以提高太阳能电池的转换效率。
具体实施方式
下面将对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅是本发明的一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其它实施例，都属于本发明保护的范围。
本发明实施例公开了一种用于太阳能电池的超细银粉的制备方法，包括以下步骤：
为了解决上述技术问题，本发明实施例公开了一种用于太阳能电池的超细银粉的制备方法，包括以下步骤：
（1）、将抗坏血酸溶液加热至50-60摄氏度，加入分散剂的同时进行搅拌，加入后继续搅拌3-3.5小时，得到还原性溶液，在还原性溶液中加入无水酒精和甲醛，搅拌30分钟，冷却至室温；
（2）、将还原性溶液和硝酸银溶液分别加热至反应温度，将硝酸银溶液加入到还原性溶液中，搅拌；
（3）、将反应后的反应物沉淀，过滤，洗涤，然后恒温干燥；
（4）、将干燥后的固体过20微米筛，得到超细银粉；
（5）、将超细银粉用于太阳能电池的正面银浆。
在本发明的一较佳实施例中，步骤（1）中的抗坏血酸溶液加热温度为55摄氏度，继续搅拌时间为200分钟。
在本发明的一较佳实施例中，步骤（2）中反应温度为120摄氏度。
在本发明的一较佳实施例中，步骤（3）中洗涤用去离子水或者无水酒精。
在本发明的一较佳实施例中，步骤（4）中的恒温为75摄氏度，干燥时间为3.2小时。
在本发明的一较佳实施例中，步骤（1）中分散剂为羧甲基纤维素。
相较于现有技术，本发明的制备方法所获得的超细银粉的纯度较高，可以提高太阳能电池的转换效率。
以上所述仅为本发明的实施例，并非因此限制本发明的专利范围，凡是利用本发明说明书内容所作的等效结构或等效流程变换，或直接或间接运用在其它相关的技术领域，均同理包括在本发明的专利保护范围内。

Claims (6)

1.一种用于太阳能电池的超细银粉的制备方法，其特征在于，包括以下步骤：
（1）、将抗坏血酸溶液加热至50-60摄氏度，加入分散剂的同时进行搅拌，加入后继续搅拌3-3.5小时，得到还原性溶液，在还原性溶液中加入无水酒精和甲醛，搅拌30分钟，冷却至室温；
（2）、将还原性溶液和硝酸银溶液分别加热至反应温度，将硝酸银溶液加入到还原性溶液中，搅拌；
（3）、将反应后的反应物沉淀，过滤，洗涤，然后恒温干燥；
（4）、将干燥后的固体过20微米筛，得到超细银粉；
（5）、将超细银粉用于太阳能电池的正面银浆。
2.根据权利要求1所述的用于太阳能电池的超细银粉的制备方法，其特征在于，步骤（1）中的抗坏血酸溶液加热温度为55摄氏度，继续搅拌时间为200分钟。
3.根据权利要求1所述的用于太阳能电池的超细银粉的制备方法，其特征在于，步骤（2）中反应温度为120摄氏度。
4.根据权利要求1所述的用于太阳能电池的超细银粉的制备方法，其特征在于，步骤（3）中洗涤用去离子水或者无水酒精。
5.根据权利要求1所述的用于太阳能电池的超细银粉的制备方法，其特征在于，步骤（4）中的恒温为75摄氏度，干燥时间为3.2小时。
6.根据权利要求1所述的用于太阳能电池的超细银粉的制备方法，其特征在于，步骤（1）中分散剂为羧甲基纤维素。
CN2013102269380A 2013-06-08 2013-06-08 用于太阳能电池的超细银粉的制备方法 Pending CN103286320A (zh)